A) VISIBLE
Several kinds of windows available:
- With AR coating
- Laminated, with/without AR coating
- Float glass and Iron Free glass
- Borosilicate
B) IR 5 μm
CaF2 (PDF properties and curves)
- Max Temperature: 1360 °C
- Transmission > 90% from 0.13 to 8µm (depending on thickness)
- Thickness: from 0.8 to 5 mm
- Size: up to 100mm
BaF2 (PDF properties and curves)
- Max Temperature: 1280 °C
- Transmission > 90% from 1.5 to 12µm (depending on thickness)
- Transmission with coating > 99% at 10.6µm
- Thickness: from 12mm
- Size: up to 150mm
MgF2 (PDF properties and curves)
- Max Temperature: 1225 °C
- Transmission > 90% from 0.11 to 7.5µm (depending on thickness)
- Thickness: from 12 mm
- Size: up to 150mm
Sapphire (PDF properties and curves)
- Max Temperature: 2000 °C
- Transmission > 80% from 0.3 to 5µm (depending on thickness)
- Thickness: from 0.8 to 10 mm
- Size: up to 160mm
C) IR 8..14 μm
Germanium (PDF properties and curves)
- Max Temperature: 90 °C
(above 90 °C, transmission decreases and goes back to normal values when temperature decreases)
- Coating AR/AR at 8..14 μm
- Coating AR/AR at 8..14 μm + Carbon Coating
- Carbon Coating Vickers hardness: 16 GPa
- Thickness: from 1 to 16 mm
- Size: up to 250 mm
Zns Water Clear (PDF properties and curves)
- Max Temperature: 300 °C (with coating)
- Transmission > 70% from 0.2 a 14 μm w/o coating
- Coating AR/AR at 8..14 μm (T > 99% at 10.6 μm)
- Thickness: up to 12mm
- Size: dia up to 250mm; squared: up to 250x200mm
Zns - Flir (PDF properties and curves)
- Max Temperature: 300 °C (with coating)
- Transmission w/o coating > 70% from 8 to 10µm (depending on thickness)
- Coating AR/AR at 8..14 μm
- Thickness: up to 12mm
- Size: dia up to 250mm; squared: up to 250x200mm
ZnSe (PDF properties and curves)
- Max Temperature: 600 °C
- Transmission range: 0,6..24 μm
- Coating AR/AR at 8..14 μm (T > 99% at 10.6 μm)
- Thickness: up to 15 mm
- Size: dia up to 250 mm; squared: up to 250 x 200 mm
|