IR MATERIALS

A) IR Fused silica (PDF Properties and curves)

  • Max temperature:
    1150° C - continuous
    1300° C - limited time
  • Transmission > 90% da 0.2 a 3.5 µm
  • Available in several sizes and thicknesses

 

B) Sapphire (PDF Properties and curves)

  • Max temperature: 2000° C
  • Transmission > 80% from 0.3 to 5.0 µm (depending on thickness)
  • Thickness from 0,8 to 10.0 mm
  • Size up to 160 mm

C) Silicon w/o AR coating (PDF Properties and curves)

  • Transmission up to 16 µm
  • Thickness from 1 to 10 mm
  • Size up to 160 mm
  • Silicon w/o O2 also available

 

D) Germanium (PDF Properties and curves)

  • Max temperature: 90° C
  • (above 90 °C, transmission decreases and goes back to normal values when temperature decreases)
  • Coating AR at 8..14 µm
  • Coating AR at 8..14 µm + Carbon Coating
  • Carbon Coating Vickers hardness 16 Gpa
  • Thickness from 1 to 16 mm
  • Size up to 250 mm

E) CaF2 (PDF Properties and curves)

  • Max temperature: 1360° C
  • Transmission 90% from 0.13 to 5.0 µm (depending on thickness)
  • Thickness up to 12 mm
  • Size up to 200 mm

 

 

F) BaF2 (PDF Properties and curves)

  • Max temperature: 1280° C
  • Transmission 90% from 0.15 to 12.5 µm (depending on thickness)
  • Transmission with coating 99% at 10.6 µm
  • Thickness from 12 mm
  • Size up to 150 mm

 

G) MgF2 (PDF Properties and curves)

  • Max temperature: 1225° C
  • Transmission 90% from 0.11 to 7.5 µm (depending on thickness)
  • Thickness up to 12 mm
  • Size up to 150 mm

 

H) ZnS - Water Clear (PDF Properties and curves)

  • Max temperature: 300° C (with coating)
  • Transmission w/o coating 70% from 0.2 to 14 µm (depending on thickness)
  • Coating AR/AR at 8..14 µm (T 99% a 10.6 µm)
  • Thickness up to 12 mm
  • Size: dia up to 250mm; squared: up to 250x200mm

 

I) ZnS - Flir (PDF Properties and curves)

  • Max Temperature: 300 °C (with coating)
  • Transmission w/o coating > 70% from 8 to 10µm (depending on thickness)
  • Coating AR/AR at 8..14 μm
  • Thickness: up to 12mm
  • Size: dia up to 250mm; squared: up to 250x200mm

 

L) ZnSe (PDF Properties and curves)

  • Max Temperature: 600 °C
  • Transmission range: 0.6..24 μm
  • Coating AR/AR at 8..14 μm (T > 99% at 10.6 μm)
  • Thickness: up to 15 mm
  • Size: dia up to 250 mm; squared: up to 250 x 200 mm

 



Germanium - ZnSe